| Título : | Effect of cerium loading on structure and morphology of modified Ce-USY zeolites |
| Autor : | Garcia, Fillipe Augusto da Costa Araújo, Daniel Ribeiro Silva, Júnia Chaves Marinho e Macedo, Julio Lemos de Ghesti, Grace Ferreira Dias, Sílvia Cláudia Loureiro Dias, José Alves Rocha Filho, Geraldo N. |
| Assunto:: | Zeólitas Óxido de cério Troca iônica Espectroscopia de Raman Ressonância magnética nuclear |
| Fecha de publicación : | oct-2011 |
| Editorial : | Sociedade Brasileira de Química |
| Citación : | GARCIA, Fillipe A. C. et al. Effect of cerium loading on structure and morphology of modified Ce-USY zeolites. Journal of the Brazilian Chemical Society, São Paulo, v. 22, n. 10, p. 1894-1902, out. 2011. DOI: http://dx.doi.org/10.1590/S0103-50532011001000010. Disponível em: http://www.scielo.br/scielo.php?script=sci_arttext&pid=S0103-50532011001000010&lng=en&nrm=iso. Acesso em: 12 jan. 2021. |
| Resumen : | Este trabalho descreve detalhadamente o efeito da quantidade de cério na estrutura e morfologia da zeólita NH4USY. Ce-USY (2-25% m/m de CeO2) foi obtido por impregnação úmida de CeCl3 seguida de calcinação a 550ºC por 8 h. Em quantidades baixas (2-10%), foi observado que as espécies de cério encontram-se nas posições de troca iônica na rede, enquanto em maiores teores (15-25%) pequenos agregados formaram-se na superfície da HUSY. Difratometria de raios X (XRD) mostrou apenas reflexões relacionadas à HUSY, confirmando a alta dispersão das espécies de cério, porém as análises por espectroscopia Raman com transformada de Fourier (FT-Raman) detectaram CeOx para os materiais acima de 10%. A reação do CeCl3 com NH4USY produziu NH4Cl, o qual se decompõe em HCl, ocasionando a desaluminização da rede. Os materiais apresentaram um aumento da razão Lewis/Brønsted com o aumento da quantidade de cério, devido a interação do excesso de cério com os grupos OH da USY e consequente formação de espécies CeOx. |
| Abstract: | This work describes comprehensibly the effect of cerium loading on the structure and morphology of NH4USY zeolite. The Ce-USY (2-25 wt.% of CeO2) was obtained by wet impregnation of CeCl3 followed by calcination at 550ºC for 8 h. At low loadings (2-10%), cerium species are mainly located at ion exchange positions in the framework, whereas at higher loadings (15-25%), small aggregates were formed on the HUSY surface. X-ray diffractograms (XRD) exhibited only the reflections related to HUSY, demonstrating the high dispersion of cerium species, but Fourier transform Raman spectroscopy (FT-Raman) detected CeOx for the materials above 10%. Reaction of CeCl3 with NH4USY produced NH4Cl, which decomposed to form HCl, leading to framework dealumination. The materials showed an increased Lewis/Brønsted ratio with increasing cerium loadings due to the interaction between the excess cerium and the OH groups of USY, and the consequent formation of CeOx species. |
| metadata.dc.description.unidade: | Instituto de Química (IQ) |
| Licença:: | Journal of the Brazilian Chemical Society - All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License (CC BY NC 4.0). Fonte: https://www.scielo.br/scielo.php?script=sci_arttext&pid=S0103-50532011001000010&lng=en&nrm=iso&tlng=en. Acesso em: 12 jan. 2021. |
| DOI: | https://dx.doi.org/10.1590/S0103-50532011001000010 |
| Aparece en las colecciones: | Artigos publicados em periódicos e afins |
Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.