Título:	Cerium–zirconium mixed oxide synthesized by sol-gel method and its effect on the oxygen vacancy and specific surface area
Autor(es):	Campos, Pablo Teles Aragão Oliveira, Claudinei Fabiano Lima, João Pedro Vieira Silva, Daniele Renata de Queiroz Dias, Sílvia Cláudia Loureiro Dias, José Alves
E-mail do autor:	mailto:jdias@unb.br
Assunto:	Nanoestruturas Óxido de zinco Óxido de cério
Data de publicação:	2021
Editora:	Elsevier
Referência:	CAMPOS, Pablo Teles Aragão et al. Cerium–zirconium mixed oxide synthesized by sol-gel method and its effect on the oxygen vacancy and specific surface area. Journal of Solid State Chemistry, v. 307, art. 122752, mar. 2022. DOI 10.1016/j.jssc.2021.122752. Disponível em: https://www.sciencedirect.com/sdfe/reader/pii/S0022459621007970/pdf. Acesso em: 22 ago. 2022.
Abstract:	In this study, cerium-zirconium mixed oxides were prepared using the sol-gel methodology with cetyltrimethylammonium bromide (CTAB) for tuning the specific surface area and pore volume. The composition of Ce0.8Zr0.2O2 (CZ) was selected as being one of the most active for soot oxidation, which is a concern as an environmental pollutant. The structural and morphological properties were investigated using EDXRF, XRD, SEM/EDS, Raman and N2 physisorption at low temperature. The catalytic test was evaluated by temperatureprogrammed oxidation coupled with mass spectrometry (TPO/MS). Any variation in the CTAB concentration during synthesis changed the particle size and surface area, indicating that the particle formation follows a mechanism in which the CTAB acts as capping agent. Additionally, the material synthesized with CTAB was found to have higher oxygen vacancy compared to the materials from the conventional sol-gel process. The catalytic test suggested that the material with the smallest surface area had the lowest temperature of oxidation (T50% = 400o C), which demonstrates that the oxygen vacancy parameter is essentially more important than the specific surface area itself.
Unidade Acadêmica:	Instituto de Química (IQ)
DOI:	https://doi.org/10.1016/j.jssc.2021.122752
Aparece nas coleções:	Artigos publicados em periódicos e afins

Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.