Title: Comportamento Termoelástico de Vigas SMAHC sob Flexão em duas Temperaturas
Thermoelastic Behavior of SMAHC Beams Subjected to Bending Loads at two Temperatures
Authors: Faluhelyi, Peter
Levy Neto, Flamínio
Silva, Edson Paulo da
Sá, Marcos V. Costa
Assunto:: Ligas de níquel-titânio
Vigas
Estruturas metálicas
Issue Date: 2013
Publisher: Rede Latino-Americana de Materiais
Citation: FALUHELYI, Peter et al. Comportamento Termoelástico de Vigas SMAHC sob Flexão em duas Temperaturas. Matéria, Rio de Janeiro, v. 18, n. 4, p. 1491-1500, dez. 2013. Disponível: <http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1517-70762013000400010&lng=en&nrm=iso>. Acesso em: 16 abr. 2018. doi: http://dx.doi.org/10.1590/S1517-70762013000400010.
Abstract: Neste trabalho, foi desenvolvido e caracterizado um compósito híbrido com memória de forma (SMAHC) por meio de uma análise teórico-experimental, no regime elástico, envolvendo a fabricação de vigas laminadas. A viga híbrida foi confeccionada em matriz de epóxi reforçada com fios de SMA e mantas de fibras picadas de vidro-E, com e sem bolsa de vácuo, de cura a frio e quente. A viga possui duas camadas de fios, com e sem roving, afastadas simetricamente o máximo possível do plano médio. Também foram produzidas vigas semelhantes, com e sem fios de aço galvanizado. Os módulos de elasticidade à flexão das vigas foram comparados aos módulos de simulações analíticas. O principal objetivo foi avaliar o aumento controlado da rigidez à flexão quando os fios de Ni-Ti (SMA) foram aquecidos, por efeito Joule, de 25°C a 69°C. As vigas de SMAHC, com fração volumétrica de Ni-Ti até 2%, tiveram um aumento no módulo de elasticidade de até 6,53%, apenas mudando a fase dos fios de martensita (25ºC) para austenita (69ºC).
Abstract: In this paper, a shape memory alloy hybrid composite (SMAHC) was developed and characterized by theoretical and experimental analysis, in the elastic regime, involving the fabrication of laminated beams. The hybrid beam was made of epoxy matrix reinforced with SMA wires and E-glass chopped mat, with and without vacuum bag, as well as cold and hot curing. The two plies incorporating wires reinforced with roving or not, were symmetrically distributed along the thickness direction, as far as possible from the beam´s middle surface. Similar specimens were also produced, substituting the Ni-Ti (SMA) wires by cheaper galvanized steel wires. The flexure elasticity modulus of the beams was compared with those obtained analytically. The main objective was to evaluate the bending stiffness of the beams, when the temperature of the Ni-Ti wires was increased by Joule effect, from 25 ºC and 69 ºC. The SMAHC beams, with volume fraction of Ni-Ti up to 2%, presented an increase in the modulus, up to 6.53 %, by changing the phase of the wires, from the martensite (25 ºC) to the austenite (69 ºC).
Licença:: Matéria (Rio de Janeiro) - All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License (CC BY NC 4.0). Fonte: http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1517-70762013000400010&lng=en&nrm=iso&tlng=pt. Acesso em: 16 abr. 2018.
DOI: http://dx.doi.org/10.1590/S1517-70762013000400010
Appears in Collections:ENM - Artigos publicados em periódicos

Show full item record Recommend this item " class="statisticsLink btn btn-primary" href="/handle/10482/28991/statistics">



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.